Depending on the type of material and with what type of paint we will use different primers to ensure adhesion to the substrate
P-07
Kind
BASE
PRODUCT
Color finish
IDEAL FOR
All kind
water
Mono-component
Transparent
y color
POROSAS
Surfaces
P-35
Epoxi base
Solvent
Bi componente
Transparent
METALIC &
CONCRET
P-31
base Poliurethan
water
Bi componente
Transparent
METALIC &
CONCRET
​
P-33
Epoxi-vinilic
Solvent
Bi componente
Only color
Metal
anticorrosive
Recomendation
Help performance and respect changes in tone
​
For those who need solvent-based primer,
maximum adherence
​
For those who need water-based primer, without solvents
Color printing,
anticorrosive
greater coverage
MATERIAL
(type of support)
Brick
Enameled Brick
Cement
Microcement
Tile
Gresite Stoneware
Granite
Natural stone
Marble
Artificial stone
Stainless steel
Carbon Steel
Galvanised steel
Steel cut
Extruded aluminum
Molded aluminum
Molten steel
Brass
Madera Exterior
Concrete
Stainless steel
Carbon Steel
Galvanised steel
Steel cut
Extruded aluminum
Molded aluminum
Molten steel
Brass
3
pEINTS
(type of support)
Acrylic paint
Synthetic Painting
​
​
​
​
Plastic paints
Pint. EPOXI base
Exterior Glaze
Synthetic enamel
Pint. Polyurethane (solv)
Pint. Polyester
Synthetic enamel
Pint. Polyurethane (water)
PRIMERS PLX COATS
IMPRIMACION (All-Terrain)(07)
Sealing primer for PLX CRISTAL System on POROSAS surfaces,
Improves the performance in m2 / liter and avoids the change of tonality.
Performance: 6-8 m2 / liter.
Finish:
Brightness (P-07),
Color (P-09) range gray, red, green and black.
Surfaces where it can be applied:
Brick, Enameled Brick, Cement, Microcement, Concrete, Tile, Gresite Stoneware, Granite, Natural Stone, Marble, Artificial Stone
Application:
It is not diluted: ready for use.
Drying: 1-2 hours to apply PLX CRISTAL (23º 60% RH)
Monocomponent
Clean the surface to be protected from dust and dirt.
It can be applied by brush, roller or gun.
Application temperature between 10 and 30
Sealer primer for PLX CRYSTAL System on exterior wood and Metal surfaces
Improves performance in m2 / liter and adhesion.
Performance: 6-8 m2 / liter.
Bicomponent A + B
Finish:
Transparent Brightness (P-32)
PROTECT-V (35)
Surfaces where it can be applied:
Metals ...
Aplicación
Monocomponente​
SUPERFICIES LISAS o PINTADAS:
Aplicar una capa de producto sin disolver.
Aplicar una capa con rodillo o pistola procurando una distribución homogénea del producto.
IMPRI-PUR (31)
Imprimación selladora para Sistema PLX CRISTAL en supeficies metálicas, hormigón, vinilos
Mejora el rendimiento en m2/litro y la adherencia.
​
Rendimiento: 6-8 m2/litro.
Bicomponente A+B
​
Acabado:
Transparente Brillo (P-31)
​
Superficies donde se puede aplicar:
Acero Inoxidable, Acero al Carbono, Acero Galvanizado, Acero corten, Aluminio extrudado, Aluminio moldeado, Acero fundido, Laton
Aplicación:
No se diluye: listo para su uso.
Secado: 4-6 horas para aplicar PLX CRISTAL (23º 60%HR)
Proporción: 9 base :1 solidificador
Limpiar de polvo y suciedad la superficie a proteger.
Se puede aplicar a brocha, rodillo o pistola.
Temperatura aplicación entre 10 y 30ª
​
Superficie muy porosas aplicar 2 capas
IMPRI-PHOS (33)
Imprimación selladora para Sistema PLX CRISTAL en supeficies METÁLICAS, ANTICORROSIVA, se fabrica en color blanco.
Mejora el rendimiento en m2/litro y la adherencia.
​
Rendimiento: 6-8 m2/litro.
​
Acabado:
Color Blanco (P-33)
Superficies donde se puede aplicar:
Acero Inoxidable, Acero al Carbono, Acero Galvanizado, Acero corten, Aluminio extrudado, Aluminio moldeado, Acero fundido, Laton
Caracteristicas:
No se diluye: listo para su uso.
Secado: 15-20 minutos para aplicar PLX CRISTAL (23º 60%HR)
Proporción: 6 base :1 solidificador
Limpiar de polvo y suciedad la superficie a proteger.
Se puede aplicar a brocha, rodillo o pistola.
Temperatura aplicación entre 10 y 30ª
​